Space Helps Nanofiller Keep Flames at Bay

If materials scientists accompanied their research with theme songs, a team from the National Institute of Standards and Technology (NIST) and the A. James Clark School of Engineering at the University of Maryland (UMD) might be tempted to choose the garage punk song "Don't Crowd Me"^* as the anthem for the promising, but still experimental nanocomposite fire retardants they are studying.

That's because the collaborators, including NIST guest researcher and Department of Fire Protection Engineering research professor Takashi Kashiwagi and Department of Materials Science and Engineering postdoctoral research associate Xin Zhang, have demonstrated that the more widely and uniformly dispersed nanoscale plates of clay are in a polymer, the more fire protection the nanocomposite material provides.

Writing in the journal Polymer, the team reports that in tests of five specimens—each with the same amount of the nanoscale filler (5 percent by weight)—the sample with the most widely dispersed clay plates was far more resistant to igniting and burning than the specimen in which the plates mostly clustered in crowds. In fact, when the two were exposed to the same amount of heat for the same length of time, the sample with the best clay dispersion degraded far more slowly. Additionally, its reduction in mass was about a third less.

In the NIST/UMD experiments, the material of interest was a polymer—a type of polystyrene, used in packaging, insulation, plastic cutlery and many other products—imbued with nanometer scale plates of montmorillonite, a type of clay with a sandwich-like molecular structure. The combination can create a material with unique properties or properties superior to those achievable by each component—clay or polymer—on its own.

Over the past decade, polymer-montmorillonite nanocomposites have attracted significant research and commercial interest. Studies have suggested that how the clay plates disperse, stack or clump in polymers dictates the properties of the resultant material. However, the evidence—especially when it comes to the flammability properties of the nanocomposites—has been somewhat muddy.

Led by Kashiwagi, the NIST-UMD team subjected their clay-dispersion-varying samples to an exhaustive battery of characterization methods and flammability tests. Affording views from the nanoscopic to the microscopic, the array of measurements and flammability tests yielded a complete picture of how the nanoscale clay plates dispersed in the polymer and how the resultant material responded when exposed to an influx of heat.

The researchers found that with better dispersion, clay plates entangle more easily when exposed to heat, thereby forming a network structure that is less likely to crack and leading to fewer gaps in the material. The result, they say, is a heat shield that slows the rate of degradation and reduces flammability. The NIST team, led by Rick Davis, is now exploring other approaches to reduce flammability, including the use of advanced materials and novel coating techniques.

^* Keith Kessler, "Don't Crowd Me." Story courtesy of and adapted from the original by Mark Bello, National Institute of Standards and Technology.

For More Information:

M. Liu, X. Zhang, M. Zammarano, J.W. Gilman, R.D. Davis and T. Kashiwagi. "Effect of Montmorillonite dispersion on flammability properties of poly(styrene-co-acrylonitrile) nanocomposites." Polymer Vol. 52, Issue 14, June 22, 2011.

Published August 1, 2011